Place of Origin : Jiangsu, China
Payment Terms : L/C, T/T, Western Union
Supply Ability : 10000 Piece/Pieces per Month
Delivery Time : 7-15 work days
Material : Zirconia Ceramic, Engineering ceramics
Application : Structure Ceramic, Industrial Equipment
Processing Service : Custom processing
Material option : Customizable
Quality control : 100% Inspection
Drawing Format : 2D/(PDF/CAD)3D(IGES/STEP)
MOQ : 50 Pieces
Zirconia Ceramic Parts
high quality zirconia ceramic parts;
Molding process is mainly hot, dry pressure, isostatic pressing;
Products alumina purity to meet customer requirements, tolerances can be controlled within ± 0.001mm range;
Surface roughness can reach Ra0.2um, for deep processing, the surface roughness can be controlled below Ra0.02um;
According to the use of ceramic pieces of the environment, recommend the best solution for customers.
Zirconia Ceramic Performance Table | |||
Property | Item | Data | Unit |
Mechanical Characteristics | Color | Ivory | - |
Density | 6.02 | g/cm3 | |
Bending Strength | 800 | MPa | |
Compressive trength | 3000 | MPa | |
Elastic Modulus | 200 | GPa | |
Fracture Toughness | 8 | MPa m1/2 | |
Weber Coefficient | 15 | m | |
Vickers Hardness | 1200 | HV 0.5 | |
Thermal Characterics | Coefficient of Line Thermal Expansion | 10 | 10-6K-1 |
Thermal Conductivity | 3 | W/mK | |
Thermal Shock Resistance(Put in Water) | 300 | ΔT °C | |
Max Working Temperature | 1000 | °C | |
Electrical Characteristics | Volume Resistance at 20°C | >1013 | Ωcm |
Dielectric Strength | 11×106 | V/m | |
Dielectric Constant | 33 | εr | |
One MHZ Dielectric Loss Angle at 20°C | 0.0016 | tanδ | |
Chemical Characteristics | Nitric Acid (60%) 90°C | ≒0.00 | WT Loss mg/cm^2/day |
Sulphuric Acid (95%) 95°C | 0.04 | ||
Caustic Soda (30%) 80°C | 0.08 |
2.381mm 2.5mm 2mm Ceramic Zirconia Ball Bearing Zro2 Ceramic Bearing G5-25 8mm X 22mm X 7mm Images |
Friendly Links: www.everychina.com